Exploiting light-based 3D-printing for the fabrication of mechanically enhanced, patient-specific aortic grafts

This study reports on the development and characterisation of an alternative vascular graft material. An alginate:PEGDA (AL:PE) interpenetrating polymer network (IPN) hydrogel has been produced with uniaxial tensile tests revealing similar strength and stiffness (0.39 ± 0.05 MPa and 1.61 ± 0.19 MPa, respectively) to the human aorta. Moreover, AL:PE tubular conduits of similar geometrical dimensions to segments of the aorta were produced, either via conventional moulding methods or stereolithography (SLA) 3D-printing. While both fabrication methods successfully demonstrated AL:PE hydrogel production, SLA 3D-printing was more easily adaptable to the fabrication of complex structures without the need of specific moulds or further post-processing. Additionally, most 3D-printed AL:PE hydrogel tubular conduits sustained, without failure, compression up to 50% their outer diameter and returned to their original shape upon load removal, thereby exhibiting promising behaviour that could withstand pulsatile pressure in vivo. Overall, these results suggest that this AL:PE IPN hydrogel formulation in combination with 3D-printing, has great potential for accelerating progress towards personalised and mechanically-matched aortic grafts.PMID:38588633 | DOI:10.1016/j.jmbbm.2024.106531
Source: Journal of the Mechanical Behavior of Biomedical Materials - Category: Materials Science Authors: Source Type: research