Attachment of redox active molecules on the carbon additive and its effect on the cycling performance of LiFePO4 electrodes

Publication date: Available online 13 June 2019Source: Materials Chemistry and PhysicsAuthor(s): Hamidreza Saneifar, Nicolas Delaporte, Galyna Shul, Daniel BélangerAbstractThe bis(1,10-phenanthroline)-5-amino-1,10-phenanthroline iron complex (Fe2+[Phen]2[Phen-NH2]) was synthesized and characterized before covalent attachment to the surface of acetylene black carbon via diazonium chemistry. The metal complex was characterized by UV–visible spectroscopy and elemental analysis. Elemental analysis revealed a low grafting yield of approximately 3 wt%. Cycling voltammetry of modified-carbon electrode showed an apparent redox potential of 4.1 V (vs. Li) characteristic of the iron complex. The voltammetric charge associated to the redox peak corresponded to approximately 3.3 wt% of grafted groups, in agreement with the value estimated by elemental analysis. The electrochemical performance of LiFePO4 cathodes using modified and unmodified acetylene black carbons as conducting additive were compared through galvanostatic cycling and electrochemical impedance spectroscopy measurements. At a 5C rate, the electrode made with the modified carbon delivered a specific capacity of about 60 mAh.g−1 in comparison to only 25 mAh.g−1 for the composite with unmodified conductive additive. Charge/discharge cycling experiments over 200 cycles at C/2.5 revealed a capacity fade of about 0.2 and 0.14% per cycle for the LiFePO4 electrodes made with the unmodified and modified carbons, respe...
Source: Materials Chemistry and Physics - Category: Materials Science Source Type: research