The effects of Pr3+ doping on the dielectric and photoluminescence properties of BaTi0.9(Yb0.5Nb0.5)0.1O3 ceramic

Publication date: Available online 5 June 2019Source: Materials Chemistry and PhysicsAuthor(s): Zied Abdelkafi, Olivier Bidault, Issa Kriaa, Hanen AbdmoulehAbstractThe praseodymium Pr3+ doped BaTi0.9(Yb0.5Nb0.5)0.1O3 (BTYN01) ceramic, under low concentration (0.1%), was prepared by a conventional ceramic fabrication technique and its phase structure, microstructure, dielectric, vibrational and photoluminescence (PL) properties was studied. Both X-ray diffraction (XRD) and Raman studies confirmed the incorporation of Pr3+ into A-site lattice of BTYN01. The structure of Ba0.9985Pr0.0010.0005Ti0.9(Yb0.5Nb0.5)0.1O3 (BTYN01-Pr) shows the coexistence of -cubic symmetry (∼10%) and P4mm-tetragonal symmetry (∼90%) at room temperature. The dielectric study reveals that the maximum of the dielectric constant of BTYN01-Pr occurred at 283 K. The incorporation of Pr3+ has not change significantly the temperature of transition of BTYN01, but makes its transition peak more broadened. Contrary to BTYN01, doping with the Pr3+ allowed us to accommodate a PL response with a strong single red emission localized at about 648 nm. The temperature dependence on up-conversion emissions of BTYN01-Pr ceramic, obeying an Arrhenius law with a weak energy activation (Ea=0.04 eV), indicates that the mechanism of PL emission is probably related to the vibrational property of the lattice. The Pr3+ doped BTYN01 red emission material with dielectric properties might have important technological promise in n...
Source: Materials Chemistry and Physics - Category: Materials Science Source Type: research