Untapped Potential of Food Waste Derived Biochar for the Removal of Heavy Metals from Wastewater

This study implies the introduction of novel method of converting food waste (FW) to biochar through pyrolysis, examine its physiochemical characteristics, and investigate its adsorption potential for the removal of heavy metals from water. The results revealed that biochar yield decreased from 18.4 % to 14.31 % with increase in pyrolysis temperature from 350 to 550 ºC. Likewise, increase in the pyrolysis temperature also resulted in the increase in the ash content from 39.87 % to 42.05 % thus transforming the biochar into alkaline nature (pH 10.17). The structural and chemical compositions of biochar produced at various temperatures (350, 450, and 550 ºC) showed a wide range of mineralogical composition, and changes in the concentration of surface functional groups. Similarly, the adsorption potential showed that all the produced biochar effectively removed the selected heavy metals from wastewater. However a slightly high removal capacity was observed for biochar produced at 550 ºC that was credited to the alkaline nature, negatively charged biochar active sites due to O-containing functional groups and swelling behavior. The results also showed that the maximum adsorption was recorded at pH 8 at adsorbent dose of 2.5 g L-1 with the contact time of 120 min. To express the adsorption equilibrium, the results were subjected to Langmuir and Freundlich isotherms and correlation coefficient implies that the adsorption process follows the Freundlich adsorption isotherm. The fi...
Source: Chemosphere - Category: Chemistry Authors: Source Type: research