Characteristic fatigue strength and reliability of dental glass-ceramics: Effect of distinct surface treatments - Hydrofluoric acid etching and silane treatment vs one-step self-etching ceramic primer

J Mech Behav Biomed Mater. 2023 Dec 22;150:106338. doi: 10.1016/j.jmbbm.2023.106338. Online ahead of print.ABSTRACTThe aim of this study was to mechanically characterize through flexural fatigue test two CAD-CAM glass-ceramics according to distinct surface etching protocols. To do so, feldspathic (FELD) and lithium disilicate (LD) glass ceramics were subjected to different surface treatments: (1) control - no treatment (Ctrl); (2) conventional protocol etching with 5% hydrofluoric acid followed by silane coupling agent application (HF + SIL; Monobond N, Ivoclar); or (3) using a self-etching ceramic primer (E&P; Monobond Etch & Prime, Ivoclar). Ceramic discs (N = 120; Ø = 12 mm; thickness = 1.2 mm) were produced from CAD-CAM blocks, with 60 being from FELD (VITABLOCS Mark II, Vita Zahnfabrik) and 60 from LD (IPS e.max CAD, Ivoclar). Next, 20 disks of each ceramic were allocated into three groups: Ctrl, HF + SIL, or E&P. Surface roughness data were collected on all samples before and after surface treatments (except for Ctrl). Cyclic fatigue (n = 15) biaxial flexural strength tests were performed by the piston-on-three-balls geometry (ISO 6872) considering the test parameters established from a monotonic test (n = 5). The monotonic test was carried out at a 1 mm/min loading rate and 500 kgf loading cell until fracture to obtain the failure data. The cyclic fatigue test was executed underwater at a frequency up to 20 Hz, with the first stress being 25% of the monoto...
Source: Journal of the Mechanical Behavior of Biomedical Materials - Category: Materials Science Authors: Source Type: research