Fabrication and characterisation of a polyamide thin-film composite membrane on a nylon 6,6 substrate for isopropanol dehydration

Publication date: Available online 19 September 2019Source: Comptes Rendus ChimieAuthor(s): Wan Zulaisa Amira Wan Jusoh, Sunarti Abdul Rahman, Abdul Latif Ahmad, Nadzirah Mohd MokhtarAbstractThin-film composite (TFC) is feasible for use in isopropanol (IPA) dehydration by pervaporation (PV) for its superior performance and strength. The hydrophobic substrate membrane allows the penetration of the diamine monomer into the pores, which leads to flux reduction. Furthermore, hydrophobic polymer is difficult for TFC deposition because of its strong and opposing characteristics. To solve this problem, hydrophilic nylon 6,6 (N66) was introduced as a substrate in this application because of the balanced characteristics such as small distribution pores, great interaction with polyamide layer, and high mechanical strength to overcome the swelling weakness. TFC membranes were prepared by interfacial polymerisation (IP) method between m-phenylenediamine (MPD) and trimesoyl chloride (TMC) monomer. The chemical and physical properties were characterised by scanning electron microscopy (SEM), Fourier-transform infrared (FTIR) spectroscopy, contact angle, and swelling test analyses. A fully aromatic polyamide group was detected at FTIR spectrum 1609–1610 cm−1. Increasing the immersion time from 2 to 5 min in 2 wt % MPD and 1 min immersion in 0.1 wt % TMC solutions increased the thickness of the membranes from 40.0 to 56.3 μm. The contact angle decreased significantly from 50° to...

Source: Comptes Rendus Chimie - September 19, 2019 Category: Chemistry Source Type: research