Revealing the composite fretting-corrosion mechanisms of Ti6Al4V alloy against zirconia-toughened alumina ceramic in simulated body fluid

In this study, the tangential-radial composite fretting was realized by applying a normal alternating load to the tangential fretting. The composite fretting corrosion behavior of zirconia toughened alumina ceramic/Ti6Al4V alloy used for the head-neck interface of an artificial hip joint under simulated body fluid was investigated. The effects of displacement and alternating load amplitude were considered. The alternating load amplitude was given by the maximum normal load and minimum normal load ratio R. The results showed that the composite fretting damage mechanisms of this pair were mainly abrasion and tribocorrosion. Cracking also existed under large displacement. The effect of alternating load on fretting corrosion was found to be mainly caused by changes in the contact area and instantaneous contact state. In addition, the alternating load during the composite fretting promoted the formation of the three-body layer in the contact area. A decrease in load ratio caused fretting to change from gross to partial slip. In the case of small displacement, the load ratio had little effect on the friction work or wear scar profile. The corrosion rate of materials and the concentration of metal ions released into the solution increased as load ratio decreased. In cases of large and medium displacement, load ratio reduction increased the friction work and expanded the wear scar. The reduction in load ratio also caused the corrosion rate of the material to increase and then decreas...
Source: Journal of the Mechanical Behavior of Biomedical Materials - Category: Materials Science Authors: Source Type: research