Effect of hydrophilic silica and dual coagulation bath on structural and mechanical properties of PVDF membrane for membrane distillation

In this study, the synergetic effect of SiO2 nanoparticles as well as employing the dual coagulation bath on physical and mechanical properties of Polyvinylidene Fluoride (PVDF) flat-sheet membranes produced by dry-wet phase inversion (DIPS) technique has been investigated. The results of microstructural analysis using Scanning Electron Microscope (SEM) demonstrated that by adding nanoparticles while the pore size decreased noticeably, the percentage of porosity significantly increased. Also, it has been revealed that by utilizing isopropanol as the first coagulation bath the finger-like macro-voids became smaller in size, and the share of sponge-like structures rose remarkably. The membrane performance was tested by Vacuum Membrane Distillation (VMD) for measuring the flux and Liquid Entry Pressure (LEPw) laboratory setup. It can be seen that by increasing the content of SiO2 nanoparticles to 6 wt.% while the LEPw approximately halved, the flux soared to about 10000 g/m2h. Moreover, mechanical testing showed that although the tensile strength of nanocomposite samples fabricated in isopropanol dual coagulation bath was improved by up to 66%, their ductility slightly declined. Furthermore, the hydrophobicity of each membrane was examined via contact angle measurements. Finally, it was found that all membranes completely rejected the NaCl in rejection test.Graphical abstract
Source: Journal of Environmental Health Science and Engineering - Category: Environmental Health Source Type: research